PC红外线穿透PC
红外透过起始阈
|
|
nm |
575 |
650 |
700 |
780 |
|
红外透过率(2mm 厚度) |
|
- |
|
|
|
>85%(900-1100nm) |
|
可见光透过率(400- 700nm) 2mm 厚度 |
|
- |
|
<3.0% |
<1.0% |
<1.0% |
|
折射率 |
|
- |
|
1.59 |
1.59 |
1.59 |
|
熔融指数 |
|
g/10min |
11 (300℃,1.2KG) |
11 (300℃,1.2KG) |
11 (300℃,1.2KG) |
11 (300℃,1.2KG) |
|
密度 |
|
g/cm3 |
1.2 |
1.2 |
1.2 |
1.2 |
|
吸水率,24H |
|
% |
0.15 |
0.15 |
0.15 |
0.15 |
|
表面铅笔硬度(1kgf) |
|
- |
HB |
HB |
HB |
HB |
|
洛氏硬度 |
|
- |
70 |
70 |
70 |
70 |